45CrNi4Mo/1.2767 Hot Work Tool Steel Plates Bars Sheet Forgings

Contact Now* Send an Inquiry to this supplier.
or
Start Order * Name your price

Quick Information

  • Place of Origin: China
  • :

Description

45CrNi4Mo /1.2767 Hot Work Tool Steel Plates Bars Sheet Forgings

Product Details

Chemical composition

C

Mn

Si

Cr

V

Mo

P

S

0.40-0.50

0.15-0.45

0.10-0.40

1.20-1.50

-

0.15-0.35

≤0.03

≤0.03

Equivalent grades:

DIN

W.Nr.

AFNOR

JIS

BS

SIAU

GB,YB

X45NiCrMo4

1.2767

Y35NCD16

-

-

-

45CrNi4Mo

Application
Ni Cr Mo steel  characterized by high level harden-ability and toughness. Suitable for the fabrication of tools exposed to repeated impacts and strong pressure in service. Treated for maximum hardness, it can also be used to construct cold work dies for cutlery, jewelry and plastic, anvils for hammers, rams and pile drivers dies and punches for horizontal forging machines rolls for hot work bending machines. It is advisable to use the blocks for dies treated at various hardness limits according to the etching depth complying with the indications given below.

Heat treatment:

Isothermal annealing:

- Heat to 880°C, hold at temperature for 1/2 h to 1 h;

- Furnace cooling to 610°Cand hold at temperature for at least 30 hours;

- Cool by 10°C/h to 580°C;

- Cooling in air.

https://www.risunsteel.com/hot-work-tool-steel/

Following isothermal annealing with sub-critical annealing, holding at temperature for 10-12 hours, maximum. Softening is obtained with HB<270

Stress relieving:

To be carried out after maching and before the final heat treatment.

- Heat to 630°C, hold for 4-6 hours;

- Furnace cooling to 300-350°C;

- Cooling in air.

Hardening:

- Initial preheating to 350-450°C;

- Second preheating to 650-750°C;

- Heat to hardening temperature in the range 850-880°C and hold at temperature;

- Accrording to the shape and dimensions of the tool, cooling in still or forced air, possibly, in oil or in salt bath at 450-500°C;

in the latter case, as soon as the temperature of the tool is even, continue cooling in air.

Quenched hardness:54-57 HRC.

Tempering:

In the range 550-630°C for 4-6 hours according to the hardness required, the dimensions of the parts and preating conditions, cooling in still air.

Before tempering, preheat the parts to 200-300°C.

Risunsteel ,based on the over one hundred yearss production history of special steel  in Huangshi, provide professional services and material for cutting tool companies, mould companies and other industrial enterprises all over the world for years.

 


Price

  • Delivery Port : Shanghai

Packaging & Delivery

  • Delivery Lead Time : 45-90 days
  • Supply Ability : 3000 tons per month

Product Image

  • 45CrNi4Mo/1.2767 Hot Work Tool Steel Plates Bars Sheet Forgings image

Send an Inquiry to this supplier

Send an Inquiry to this supplier
* From
  To Margaret Yu
Hubei Risunsteel Co., Ltd.
* Buying Product
- Please enter your specific buying item.
e.g. 42 inch LCD TV, leather executive chair
Category : Steel Sheets
* Message

Use English only Max. 2000 characters. (Min. 20)

Send
EC21.com does not guarantee the validity of product information or the credentials of sellers.